| Properties | Test Method | Test Condition | Units | Typical Values |
| Tensile Strength (X-Y) | ISO527/2 | 50 mm/min | MPa | 55 |
| Young’s Modulus (X-Y) | ISO527/2 | 1 mm/min | MPa | 2990 |
| Elongation at Break (X-Y) | ISO527/2 | 50 mm/min | % | 17.3 |
| Flexural Strength (X-Y) | ISO178 | 2 mm/min | MPa | 77 |
| Flexural Modulus (X-Y) | ISO178 | 2 mm/min | MPa | 2226 |
| IZOD Impact Notched (X-Y) | ISO180 | 23°C | kJ/m² | 17 |
| IZOD Impact Notched (Z-X) | ISO180 | 23°C | kJ/m² | / |
| Shore Hardness | ISO868 | 23°C | HD | 80 |
| Heat Deflection Temperature (HDT) | ISO75 | 0.45 MPa | °C | 68 |
| Glass Transition (Tg) | ISO11357-3 | 10°C/min | °C | 79.4 |
| Melting Point | ISO11357-3 | 10°C/min | °C | 195 |
| Decomposition Temp @5% | ISO11358 | 20°C/min | °C | ≥423 |
| Vicat Softening Temp | ISO306 | 5kg, 50°C/h | °C | 68 |
| Mold Shrinkage | ISO294 | 23°C | % | 0.1–0.5 |
| Coefficient of Thermal Expansion | ISO11359-2 | – | μm/(m·°C) | 51 |
| Melt Flow Rate | ISO1133 | 190°C/2.16kg | g/10min | 5.3 |
| Density | ISO1183 | 23°C | g/cm³ | 1.27 |
| Volume Resistivity | IEC60093 | – | ohm-cm | 1.0E+15 |
| Dielectric Constant | IEC60250 | 1kHz | – | 2.6 |
| Flammability | UL94 | 1.5mm | Class | HB |
Recommended Printing Parameters
| Parameters | Range |
| Nozzle Print Temp. | Temperature °C s | Speed mm/ |
| 230-240 | 50-100 |
| 240-260 | 100-200 |
| Print Platform Temp. | 60-70°C |
| Print Platform Material | Normal |
| Print Platform Treatment | GLUE |
| Cool Fan | On |
| Raft Distance | 0.4-0.6mm |
| Retraction Distance | 0.8-1.2mm |
| Retraction Speed | 30-40mm/s |
| Room Temp. | Normal temperature |
| Support Material | PVA |
| Drying Temp. | 50°C |