Print3dkw BL Silk PLA Filament

Properties	Test Method	Test Condition	Unit	Typical Value
Tensile Strength (X-Y)	ISO527/2	50 mm/min	MPa	60.6
Young’s Modulus (X-Y)	ISO527/2	1 mm/min	MPa	2760
Elongation at Break (X-Y)	ISO527/2	50 mm/min	%	6.3
Flexural Strength (X-Y)	ISO178	2 mm/min	MPa	65
Flexural Modulus (X-Y)	ISO178	2 mm/min	MPa	1895
IZOD Impact Notched (X-Y)	ISO180	23°C	KJ/m²	4.2
Shore Hardness	ISO868	23°C	HD	80
Heat Deflection Temperature (HDT)	ISO75	0.45 MPa	°C	53
Glass Transition Temperature (Tg)	ISO11357-3	10°C/min	°C	60.9
Melting Point	ISO11357-3	10°C/min	°C	164
@5% Decomposition Temp.	ISO11358	20°C/min	°C	≥364
Vicat Softening Temperature	ISO306	5kg, 50°C/h	°C	54
Mold Shrinkage	ISO294	23°C	%	0.1–0.3
Thermal Expansion Coefficient	ISO11359-2		μm/(m·°C)	101×10⁻⁶
Melt Flow Rate	ISO1133	190°C/2.16kg	g/10min	9
Density	ISO1183	23°C	g/cm³	1.25
Volume Resistivity	IEC60093	–	ohm-cm	2.90E+15
Dielectric Constant	IEC60250	1kHz	–	1.51
Flammability Rating	UL94	1.5mm	Class	HB

Color	Blue, Red, White